Current Nanoscience

Author(s): Lixin Wang, Peipei Zhang, Lei Bai, Lei Cao, Jing Du, Yazhou Wang and Xiujuan Qin*

DOI: 10.2174/1573413714666180405142110

DownloadDownload PDF Flyer Cite As
Effects of Electrodeposition Time on Ni/rGO Composite Electrode as an Efficient Catalyst for Hydrogen Evolution Reaction in Alkaline Media

Page: [178 - 187] Pages: 10

  • * (Excluding Mailing and Handling)

Abstract

Background: Ni/rGO composite electrode has been fabricated by facile supergravity electrodeposition as a low-cost catalyst for efficient hydrogen evolution in alkaline media. In this paper, the electrodeposition time is the main research variable. When the electrodeposition time is 100 minutes, the Ni/rGO-100 catalyst manifests the highest electrocatalytic activity toward the hydrogen evolution reaction (HER). In 1.0 M NaOH solution, the overpotential at a current density of 100 mA cm-2, Tafel slope and charge transfer resistance of Ni/rGO-100 catalyst is 184 mV, 77 mV dec-1 and 4.173 Ω, respectively. In addition, Ni/rGO-100 catalyst shows a long-term durability at a constant current density of 100 mA cm-2 for 10 h. The outstanding HER electrocatalytic performance of the Ni/rGO-100 is mainly related to the synergetic combination of Ni and rGO, as well as the enlarged exposure of catalytically active sites and improved transport of electrons arising from the good conductivity of graphene.

Method: In a classic experiment, GO was prepared by modified Hummers method. The Ni/rGO composite electrodes were prepared by supergravity electrodeposition, which has been reported in detail in our published paper. Firstly, a ø10 cm × 2 cm Ni foam circle was cleaned sequentially in HCl solution (15%), acetone and DI water for 5 min with ultrasonication to be used as a cathode. And a pure nickel pipe was used as anode. The Ni/rGO composite cathodes were electrodeposited in a blackish green plating bath which contained 350 g L-1 Ni(NH2SO3)2·6H2O, 10g L-1 NiCl2·6H2O, 30 g L-1 NH4Cl , 1.0 g L-1 GO colloidal solution with different electrodeposition time, 10min, 30min, 60min, 80min, 100min, respectively. The pH value of the plating bath is 3.5-3.8. The above five electrodes were respectively denominated as Ni/rGO-10, Ni/rGO-30, Ni/rGO-60, Ni/rGO-80, Ni/rGO-100. All composite electrodes were performed under the strength of the supergravity with G=350 g at a current density of 3 A dm-2 at 318 K. Afterwards the Ni foam coated with Ni/rGO hybrid was taken out of the reaction vessel, followed by washing with deionized water to remove physical adsorption residua, and then dried at 80°C.

Results: In this paper, the electrodeposition time is the main research variable. When the electrodeposition time is 100 minutes, the Ni/rGO-100 catalyst manifests the highest electrocatalytic activity toward the hydrogen evolution reaction (HER). In 1.0 M NaOH solution, the overpotential at a current density of 100 mA cm-2, Tafel slope and charge transfer resistance of Ni/rGO-100 catalyst is 184 mV, 77 mV dec-1 and 4.173 Ω, respectively.

Conclusion: In summary, we have synthesized a class of composite electrodes (Ni/rGO) for HER in alkaline solution by electrodeposition under supergravity field. We studied the effect of electrodeposition time on electrode performance in detail. With the increase of electrodeposition time, the number of active sites is enlarged provided by the electrode. When the electrodeposition time is 100 min, we fabricate the best electrode (Ni/rGO-100). The η100, Tafel slope and charge transfer resistance of Ni/rGO-100 is 184 mV, 77 mV dec-1 and 4.173 Ω, respectively. The introduction of graphene and supergravity field plays a key role in improving the performance of the electrodes. This work is a pivotal part of the development of Ni/rGO as a non-precious HER catalyst for green energy field.

Keywords: Electrodeposition time, hydrogen evolution reaction, electrocatalytic performance, Ni/rGO, alkaline media, composite electrode.

Graphical Abstract

[1]
Zhang, Q.; Li, Y.; Yang, Q.; Chen, H.; Chen, X.; Jiao, T.; Peng, Q. Distinguished Cr (VI) capture with rapid and superior capability using polydopamine microsphere: Behavior and mechanism. J. Hazard. Mater., 2017, 342, 732-740.
[2]
Zhao, X.; Ma, K.; Jiao, T.; Xing, R.; Ma, X.; Hu, J.; Huang, H.; Zhang, L.; Yan, X. Fabrication of hierarchical layer-by-layer assembled diamond-based core-shell nanocomposites as highly efficient dye absorbents for wastewater treatment. Sci. Rep., 2017, 7, 44076.
[3]
Long, X.; Li, G.; Wang, Z.; Zhu, H.; Zhang, T.; Xiao, S.; Guo, W.; Yang, S. Metallic iron–nickel sulfide ultrathin nanosheets as a highly active electrocatalyst for hydrogen evolution reaction in acidic media. J. Am. Chem. Soc., 2015, 137, 11900-11903.
[4]
Chen, Z.; Ma, Z.; Song, J.; Wang, L.; Shao, G. Novel one-step synthesis of wool-ball-like Ni-carbon nanotubes composite cathodes with favorable electrocatalytic activity for hydrogen evolution reaction in alkaline solution. J. Power Sources, 2016, 324, 86-96.
[5]
Yang, W.; Yang, W.; Song, A.; Gao, L.; Sun, G.; Shao, G. Pyrrole as a promising electrolyte additive to trap polysulfides for lithium-sulfur batteries. J. Power Sources, 2017, 348, 175-182.
[6]
Lu, J.M.; Zheliuk, O.; Leermakers, I.; Yuan, N.F.; Zeitler, U.; Law, K.T.; Ye, J.T. Evidence for two-dimensional Ising superconductivity in gated MoS2. Science, 2015, 350, 1353-1357.
[7]
Huang, P.; Lethien, C.; Pinaud, S.; Brousse, K.; Laloo, R.; Turq, V.; Respaud, M.; Demortière, A.; Daffos, B.; Taberna, P.L. On-chip and freestanding elastic carbon films for micro-supercapacitors. Science, 2016, 351, 691-695.
[8]
Du, Q.; Su, L.; Hou, L.; Sun, G.; Feng, M.; Yin, X.; Ma, Z.; Shao, G.; Gao, W. Rationally designed ultrathin Ni-Al layered double hydroxide and graphene heterostructure for high-performance asymmetric supercapacitor. J. Alloys Compd., 2018, 740, 1051-1059.
[9]
Miller, Jr, W.R.; Rhoderick, G.C.; Guenther, F.R. Investigating adsorption/desorption of carbon dioxide in aluminum compressed gas cylinders. Anal. Chem., 2015, 87, 1957-1962.
[10]
Song, A.; Yang, W.; Yang, W.; Sun, G.; Yin, X.; Gao, L.; Wang, Y.; Qin, X.; Shao, G. Facile synthesis of cobalt nanoparticles entirely encapsulated in slim nitrogen-doped carbon nanotubes as oxygen reduction catalyst. ACS Sustain. Chem.& Eng., 2017, 5(5), 3973-3981.
[11]
Yin, X.; Sun, G.; Wang, L.; Bai, L.; Su, L.; Wang, Y.; Du, Q.; Shao, G. 3D hierarchical network NiCo2S4 nanoflakes grown on Ni foam as efficient bifunctional electrocatalysts for both hydrogen and oxygen evolution reaction in alkaline solution. Int. J. Hydrogen Energy, 2017, 42(40), 25267-25276.
[12]
Lv, H.; Xi, Z.; Chen, Z.; Guo, S.; Yu, Y.; Zhu, W.; Li, Q.; Zhang, X.; Pan, M.; Lu, G. C and N hybrid coordination derived Co–C–N complex as a highly efficient electrocatalyst for hydrogen evolution reaction. J. Am. Chem. Soc., 2015, 137, 5859-5862.
[13]
Zhou, W.; Wu, X.J.; Cao, X.; Huang, X.; Tan, C.; Tian, J.; Liu, H.; Wang, J.; Zhang, H. Ni3S2 nanorods/Ni foam composite electrode with low overpotential for electrocatalytic oxygen evolution. Energy Environ. Sci., 2013, 6, 2921-2924.
[14]
Wang, M.; Wang, Z.; Yu, X.; Guo, Z. Facile one-step electrodeposition preparation of porous NiMo film as electrocatalyst for hydrogen evolution reaction. Int. J. Hydrogen Energy, 2015, 40, 2173-2181.
[15]
Tasic, G.S.; Maslovara, S.P.; Zugic, D.L.; Maksic, A.D.; Kaninski, M.P.M. Characterization of the Ni–Mo catalyst formed in situ during hydrogen generation from alkaline water electrolysis. Int. J. Hydrogen Energy, 2011, 36, 11588-11595.
[16]
González-Buch, C.; Herraiz-Cardona, I.; Ortega, E.; García-Antón, J.; Pérez-Herranz, V. Synthesis and characterization of macroporous Ni, Co and Ni–Co electrocatalytic deposits for hydrogen evolution reaction in alkaline media. Int. J. Hydrogen Energy, 2013, 38, 10157-10169.
[17]
Lupi, C.; Dell’Era, A.; Pasquali, M. Nickel–cobalt electrodeposited alloys for hydrogen evolution in alkaline media. Int. J. Hydrogen Energy, 2009, 34, 2101-2106.
[18]
Oliver-Tolentino, M.A.; Arce-Estrada, E.M.; Cortés-Escobedo, C.A.; Bolarín-Miro, A.M.; Jesús, S.D.; González-Huerta, R.D.G.; Manzo-Robledo, A. Electrochemical behavior of NixW1−x materials as catalyst for hydrogen evolution reaction in alkaline media. J. Alloys Compd., 2012, 536, S245-S249.
[19]
Wang, M.; Wang, Z.; Guo, Z.; Li, Z. The enhanced electrocatalytic activity and stability of NiW films electrodeposited under super gravity field for hydrogen evolution reaction. Int. J. Hydrogen Energy, 2011, 36, 3305-3312.
[20]
Han, Q.; Liu, K.; Chen, J.; Wei, X. A study on the electrodeposited Ni–S alloys as hydrogen evolution reaction cathodes. Int. J. Hydrogen Energy, 2003, 28, 1207-1212.
[21]
Cao, Y.; Liu, J.; Wang, F.; Ji, J.; Wang, J.; Qin, S.; Zhang, L. Electrodeposited Ni–S intermetallic compound film electrodes for hydrogen evolution reaction in alkaline solutions. Mater. Lett., 2010, 64, 261-263.
[22]
Corte, D.A.D.; Torres, C.; Correa, P.D.S.; Rieder, E.S.; Malfatti, C.D.F. The hydrogen evolution reaction on nickel-polyaniline composite electrodes. Int. J. Hydrogen Energy, 2012, 37, 3025-3032.
[23]
Krstajić, N.V.; Lačnjevac, U.; Jović, B.M.; Mora, S.; Jović, V.D. Non-noble metal composite cathodes for hydrogen evolution. Part II: the Ni–MoO2 coatings electrodeposited from nickel chloride–ammonium chloride bath containing MoO2 powder particles. Int. J. Hydrogen Energy, 2011, 36, 6450-6461.
[24]
Li, Y.; Wang, L.; Song, A.; Xia, M.; Li, Z.; Shao, G. The study on the active origin of electrocatalytic water splitting using Ni-MoS2 as example. Electrochim. Acta, 2018, 268, 268-275.
[25]
Herraiz-Cardona, I.; Ortega, E.; Vázquez-Gómez, L.; Pérez-Herranz, V. Electrochemical characterization of a NiCo/Zn cathode for hydrogen generation. Int. J. Hydrogen Energy, 2011, 36, 11578-11587.
[26]
Jiménez-Marín, E.; Villalpando, I.; Trejo-Valdez, M.; Cervantes-Sodi, F.; Vargas-García, J.R.; Torres-Torres, C. Coexistence of positive and negative photoconductivity in nickel oxide decorated multiwall carbon nanotubes. Mater. Sci. Eng. B, 2017, 220, 22-29.
[27]
Jia, X.; Zhao, Y.; Chen, G.; Shang, L.; Shi, R.; Kang, X.; Waterhouse, G.I.N.; Wu, L.Z.; Tung, C.H.; Zhang, T. Ni3FeN nanoparticles derived from ultrathin NiFe‐layered double hydroxide nanosheets: An efficient overall water splitting electrocatalyst. Adv. Energy Mater., 2016, 6(10), 1502585.
[28]
Cai, W.; Liu, W.; Han, J.; Wang, A. Enhanced hydrogen production in microbial electrolysis cell with 3D self-assembly nickel foam-graphene cathode. Biosens. Bioelectron., 2016, 80, 118-122.
[29]
Wang, L.; Li, Y.; Xia, M.; Li, Z.; Chen, Z.; Ma, Z.; Qin, X.; Shao, G. Ni nanoparticles supported on graphene layers: An excellent 3D electrode for hydrogen evolution reaction in alkaline solution. J. Power Sources, 2017, 347, 220-228.
[30]
Song, A.; Cao, L.; Yang, W.; Li, Y.; Qin, X.; Shao, G. Uniform multilayer graphene-coated iron and iron-carbide as oxygen reduction catalyst. ACS Sustain. Chem.& Eng., 2018, 6(4), 4890-4898.
[31]
Du, J.; Shao, G.; Qin, X.; Wang, G.; Zhang, Y.; Ma, Z. High specific surface area MnO2 electrodeposited under supergravity field for supercapacitors and its electrochemical properties. Mater. Lett., 2012, 84, 13-15.
[32]
Liu, T.; Shao, G.; Ji, M. Electrodeposition of Ni(OH)2/Ni/graphene composites under supergravity field for supercapacitor application. Mater. Lett., 2014, 122, 273-276.
[33]
Mckone, J.R.; Sadtler, B.F.; Werlang, C.A.; Lewis, N.S.; Gray, H.B. Ni–Mo nanopowders for efficient electrochemical hydrogen evolution. ACS Catal., 2013, 3, 166-169.
[34]
Xing, R.; Jiao, T.; Liu, Y.; Ma, K.; Zou, Q.; Ma, G.; Yan, X. Co-assembly of graphene oxide and albumin/photosensitizer nanohybrids towards enhanced photodynamic therapy. Polymers, 2016, 8, 181.
[35]
Zhang, J.; Liu, H.; Shi, P.; Li, Y.; Huang, L.; Mai, W.; Tan, S.; Cai, X. Growth of nickel (111) plane: The key role in nickel for further improving the electrochemical property of hexagonal nickel hydroxide-nickel & reduced graphene oxide composite. J. Power Sources, 2014, 267, 356-365.
[36]
Zhen, W.; Ma, J.; Lu, G. Small-sized Ni (111) particles in metal-organic frameworks with low over-potential for visible photocatalytic hydrogen generation. Appl. Catal. B Environ., 2016, 190, 12-25.
[37]
Huang, Y.G.; Fan, H.L.; Chen, Z.K.; Gu, C.B.; Sun, M.X.; Wang, H.Q.; Li, Q.Y. The effect of graphene for the hydrogen evolution reaction in alkaline medium. Int. J. Hydrogen Energy, 2016, 41, 3786-3793.
[38]
Armstrong, R.D.; Henderson, M. Impedance plane display of a reaction with an adsorbed intermediate. J. Electroanal. Chem., 1972, 39, 81-90.
[39]
Zhiani, M.; Kamali, S. The recent development of efficient earth-abundant transition-metal nanocatalysts. Electrocatalysis, 2016, 7, 1-11.
[40]
Mahale, N.K.; Ingle, S.T. Electrocatalytic hydrogen evolution reaction on nano-nickel decorated graphene electrode. Energy, 2017, 119, 872-878.
[41]
Ge, J.M.; Zhang, B.; Lv, L.B.; Wang, H.H.; Ye, T.N.; Wei, X.; Su, J.; Wang, K.X.; Li, X.H.; Chen, J.S. Constructing holey graphene monoliths via supramolecular assembly: Enriching nitrogen heteroatoms up to the theoretical limit for hydrogen evolution reaction. Nano Energy, 2015, 15, 567-575.