Abstract

The niobium capacitor shows somewhat more unstable characteristics than the commercial tantalum capacitors, but it will be nonetheless considered as an excellent substitute of tantalum capacitors in the future. In this study, niobium powder is fabricated by metallothermic reduction process using K₂NbF₇ as a raw material, KCl and KF as diluents, and Na as a reducing agent. The niobium particle size greatly decreases from 0.7μm to 0.2μm as the amount of diluent increases. However, when a higher surface area of niobium powder is desired, more amounts of diluents are used in the said method. The niobium powder morphology and particle sizes are very sensitive to the amount of sodium excess, thus the particle size of niobium powder increases with increases in the amount of sodium excess. When more diluent and sodium are used, the niobium powder is contaminated further by impurities such as Fe, Cr, Ni, and others [1,2].

Keywords: Diluents, metallothermic reduction, niobium capacitor, raw material, reducing agent, tantalum capacitor.