Abstract

Background: Various interesting consequences are reported on structural, optical, and photoluminescence properties of Zn1-xSmxO (x=0, 0.01, 0.03 and 0.05) nanoparticles synthesized by sol-gel auto-combustion route.

Objective: This study aimed to examine the effects of Sm³⁺-doping on structural and photoluminescence properties of ZnO nanoparticles.

Methods: Zn1-xSmxO (x=0, 0.01, 0.03 and 0.05) nanoparticles were synthesized by sol-gel auto combustion method.

Results: XRD patterns confirmed the Sm³⁺ ion substitution through the undisturbed wurtzite structure of ZnO. The crystallite size was decreased from 24.33 to 18.46 nm with Sm³⁺ doping. The hexagonal and spherical morphology of nanoparticles was confirmed by TEM analysis. UV-visible studies showed that Sm³⁺ ion doping improved the visible light absorption capacity of Sm³⁺ iondoped ZnO nanoparticles. PL spectra of Sm3+ ion-doped ZnO nanoparticles showed an orange-red emission peak corresponding to 4G5/2→6HJ (J=7/2, 9/2 and 11/2) transition of Sm³⁺ ion. Sm³⁺ ion-induced PL was proposed with a substantial increase in PL intensity with a blue shift in peak upon Sm³⁺ content increase.

Conclusion: Absorption peaks associated with doped ZnO nanoparticles were moved to a longer wavelength side compared to ZnO, with bandgap declines when Sm³⁺ ions concentration was increased. PL studies concluded that ZnO emission properties could be tuned in the red region along with the existence of blue peaks upon Sm³⁺ ion doping, which also results in enhancing the PL intensity. These latest properties related to Sm³⁺ ion-doped nanoparticles prepared by a cost-efficient process appear to be interesting in the field of optoelectronic applications, which makes them a prominent candidate in the form of red light-emitting diodes.

Keywords: ZnO, Sm-doped ZnO, sol-gel auto-combustion method, X-ray diffraction, bandgap tunability, photoluminescence.